V. Electrodes for cold welding cast iron
| Eni CI ENi-BG11 | C: 0.7 Mn:1.0
Fe: 2.5 Cu:0.6
Ni: rem | For maximum machinability on grey cast Iron and malleable iron. A general purpose pure nickel electrode for filling up holes and casting defects, for correcting defects from machining and for building up worn sections. Recommended for use on dirty, aged and burnt cast iron. |
ENiFe-CI
ENiFe-1-BG11 | C: 1.1 Fe: 42 Ni: 54 | For high strength & toughness on ductile SG iron, including Meehanite and austenitic Ni-resist type irons. Also used for joining the aforementioned iron: and cast-iron lo steel. Excellent welding characteristics without any risk of overheatinq. |
ENiFe-CI
ENiFe-1-BG11 | C: 1.0 Mn:1.0 Si: 1.0 Ni: 54 Fe: res. | Basic-graphite special coated electrode with a recovery of 160%. Suitable for joining and repairing all types of grey cast iron, but especially for repairing large parts. This electrode has very high crack-resistance, and the weld metal has a high tensile strength. |
ENiFe-CI
ENiFe-1-BG 11 | C: 1.1 Fe: 42 Ni: 54 | Basic-graphite special coated electrode with a iron-nickel core wire. Suitable for joining and repairing all types of grey cast iron with steel. but especially for nodular cast iron. This electrode has very high crack-resistance, and high tensile-strength for the weld metal |
| ENiFe-CI ENiFe-1-BG11 | C: 1.1 Ni: 54 Fe: 43 Cu: 0.6 | Basic-graphite special coated electrode with a copper plated iron-nickel core. Suitable for joining and repairing all types o( grey cast iron with steel, but especially for nodular cast iron. This electrode has very high crack-resistance and high tensile-strength for the weld metal. |
| ESi E Fe C-2-BG 11 | C: 1.7 Si: 1.2 Mn: 0.9 Ti: + | Special basic graphite coated stick electrode for welding cast iron. Il is used for repair welding of difficult to weld, heavily contaminated and poor quality cast iron. Il is also suitable for wear-resistant overlays on cast iron parts. The weld deposit has approx. 340HB in the first two layers. |