Flux-cored wire for ABRASION-and HEAT-RESISTANT APPLICATIONS
MF10-GF-65-G7 62-64 HRC | C: 3.8 Cr:22 | C-, Cr-, B-, W-. V-alloyed flux-cored v/ire that deposits a very hard martensitic microstructure with carbides. The deposit is resistant lo strong mineral abrasion at higher temperatures. The hardness decreases by about 15% al 400°C. 25% at 600°C |
MF10-GF-65-GZ 63-64 HRC | C: 5.2 Cr:21 Mo: 7 Nb: 7 V: 1 W: 2 | High C-, Cr-, Mo-, Nb-, V-. W-alloyed flux-cored self-shielding wire which forms extremely hard carbides. This is used for hard facings to protect against extreme mineral wear. The deposit retains its wear resistance up to 650°C. At 400°C the hardness decreases bv about 4% at 650°C by about 10%. |
MF10-GF70-GCZ 66-68 HRC | C: 5 Si: 0.8 Cr: 38 B: 2 | Very high C-, Cr-, B -alloyed flux-cored wire electrode for extremely hard, non-corrosive hardfacing lo protect against high mineral wear also at high temperatures .The weld deposit has a ledeburitic structure, hearing many varied hypereutectic carbides. |
| MF10-GF-65-G 62 64 HRC | C: 5.3 Si: 1 Cr: 24,5 V: 5.5 | High C-, Cr-, V-alloyed flux-cored wire electrode for high abrasive wear. The weld deposit consists of chromium and vanadium carbides. Weld metal is not machinable. |