XII – ELECTRODES FOR ALLOYED STEEL
E6013 | C : 0,07 SI:0.3 | Medium-thick rutile cellulose coated electrode for welding in tight places. It is suitable for all-purpose applications in sturctural steel engineering, shipbuilding and vehicle construction. YS=420 TS=510 IV=>47 E=>22 approvals : TÜV, DB,Ü |
E6013 E 38 0 RC 11 | C : 0,07 SI:0.3 Mn : 0,50 | Medium-thick rutile cellulose coated electrode for welding in tight places. It is suitable for all-purpose applications in sturctural steel engineering, industrial engineering, shipbuilding and vehicle construction. YS=380 TS=500 IV=>47 E=>22 approvals : TÜV, DB,Ü |
C : 0,08 SI:0.4 | Medium-thick rutile cellulose coated electrode for welding in tight places. It is suitable for all-purpose applications in sturctural steel engineering, industrial engineering, shipbuilding and vehicle construction. YS=420 TS=510 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü | |
E6013 E 42 o RR 12 | C : 0,06 SI:0.4 | Rutile basic coated electrode with fast-flowing weld metal, suitable for welding construction elements made of structural steels up to L385N. Suitable for building bridges, pipelines, containers, vesserls and ships. The weld metal has outstanding mechanical properties and is highly crack-resistant. Suited for welding in tight places and root welding on pipes. YS=420 TS=490 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü |
E7018 E42 4 B 42 H 5 | C : 0,07 SI:0.5 | It is an all-purpose basic coated electrode for welding highly stressed joints safely. Resistant to cold crecking, easy slag removal. Very good welding characteristics, can also be used for welding in thight places. Fast solidifying weld metal, allows position welding at high. YS=420 TS=530 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü |
E7016 E42 3 B 32 H 10 | C : 0,07 Si:0.4 | Double basic coated electrode with excellent welding aharacteristics combined with outstanding mechanical properties. Very wll suited for AC welding (also with small transformers). The double coating provides optimal welding characteristics even when wlding in tight places. Smooth weld aspect, free o penetrantion notches. YS=420 TS=530 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü |
E7024 E 42 0 RR 73 | C : 0,07 Si:0,4 Mn: 0,7 | Thick rutile coated electrode with a recovery of 180%. It is suitable for all-purpose applications in structural steel engineering, industrial engineering, shipbuilding and vehicle construction. YS=420 TS=510 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü |
E7018-1 E 46 4 B32 H5 | C : 0,06 Si:0,5 Mn: 1,4 | The weld deposit has outstanding mechanical properties, making this products suitable for construction jobs with high mechanical loads. This is an all-purpose electrode, but it is typically used for welding on rails with high carbon content (up to 0,6%). YS=460 TS=600 IV=>47 E=>22 approvals : TÜV,GDL,DB,Ü |
E11018-M E 69 4 Mn 2NiCrMo BT 42 H5 | C : 0,05 Si:0,3 Mn: 1,7 Ni:2 Cr: 0,4 Mo:0,4 | Basic coated electrode for welding high strenght temperede low allowed steels, such as S500-S690 (StE500-StE690V) or N-X-TRA55-70. Preheating and immediate layer temperature acc. to the instructions of the steel manufacturer. YS=730 TS=830 IV=>47 E=>18 approvals : TÜV,GDL,DB,Ü |
E8018-G E 46 5 ZB 32 | C : 0,6 Si:0,4 Mn: 1,0 Ni:0,4 Cr: 0,6 | Basic coated electrode for weather-resistant steels. The weld deposit is resistant to weather and sea water influences. YS=460 TS=580 IV=>47 E=>22 |
| C7018-A1 E Mo D 42 | C: 0.07 Si: 0.6 Mn: 0.9 Mo: 0.5 | Basic coated Mo alloyed electrode for welding piping, boiler and line grained structural steels. Non-ageing welding metal, also thought at low temperature. Resistant to beat cracking and suited for service temperatures up to 550°C. YS=490 TS=600 IV=>47 E=25 -Aprovate: TÜV, DB |
| C7013-G EMoR12 | C: 0.07 Si: 0.8 Mn: 0.9 Mo: 0.5 | Rutile-coated Mo alloyed electrode for welding pipe and boiler steels as well as line grained structural steels. The vveld metal does not age and is also tough at low temperatures, resistant lo boat cracking and suited for service temperature up to550°C. YS=490 TS=600 IV=>47 F=>22 Approvals: TÜV |
| E8018-B2 E CrMo 1 B12H5 | C: 0.07 Si: 0.7 Mn:0.9 Cr: 1.1 Mo: 0.5 | Basic coated CrMo alloyed electrode for welding high strength joints on low alloyed tempered steels of up to 880 N/mm2. Suitable for welding creep-resistant CrMo steels in boiler and piping system construction. Temperature-resistant up to 5OO°C. Non-ageing welding deposit, resistant to alkaline solutions, heat-treatable and case-hardenable. ApprovalS: TUV, DB Annealed 30 min. al 720°C YS=600 TS=610 IV=90 E=24 |
| E9018-B3 E CrMo 2 B12 H5 | C: 0.05 Si: 0.6 Mn: 1.0 Cr:2.3 Mo:1.0 | Basic coated CrMo alloyed electrode for welding high strength joints on low alloyed tempered steels of up to 1100 N/mmq. Suitable for welding creep-resistant CrMo steels in boiler and piping system construction. Temperature-resistant up to 500°C. Non-ageing welding deposit, resistant to alkaline solutions, heat-treatable and case-hardenable. Annealed 30 min. at 760°C YS=510 TS=650 IV=80 E=22 |
| E 8015-86 E CrMo 5 B42 H5 | C: 0.06 Si: 0.5 Mn:1.0 Cr: 5.1 Mo: 0.5 | Basic coated CrMo alloyed electrode for welding joints with good mechanical properties to low alloyed quenched and subsequently tempered steels up to 1275 N/mmq. Suitable for welding heat-treatable, quenched and subsequently tempered steels as well as for lubes. resistant to caustic embrittlement for service temperatures up to 600°C. YS= 490 TS=620 W=>70 E=>17 |