Flux-cored wire for ABRASION-RESISTANT APPLICATIONS
MF10-GF-50-G 50-54 HRC | C: 3 Si: 1.8 | C-, Cr-, Si-, Mn-alloyed flux-cored wire on parts subject lo abrasive wear and medium impact. Garbage grinders. |
MF10-GF-60-GR 55-59 HRC | C: 4.8 Cr:28 B: + | The deposit has a high Cr- and C-alloyed stainless weld metal with excellent resistance» lo abrasion and medium impact. It can be used whenever high abrasion is expected. Best results are achieved by welding in two layers. Pumps. mixer parts, conveyer screws. |
MF10-CF-60-G 57-60 HRC | C: 5 Si: 1.7 | It can be used whenever high abrasion is expected. Compared with F-bb, the weld deposit of this electrode has higher temperature resistance (up to 45O°C). Best results are achieved by welding in two layers. Pumps, mixer parts, conveyer screws. |
| MF10-GF-60-GR 59-61 HRC | C: 5 Si: 1.5 Cr: 32 | It can be used whenever high abrasion is expected. Compared with F-bb, the weld deposit of this electrode has higher temperature resistance (up to 45O°C). Best results are achieved by welding in two layers. Pumps, mixer parts, conveyer screws. |
| MF10-GF-60-G 61-63 HRC | C: 5.4 Si: 1.1 Cr: 22 Nb: 7 | High C-, Cr-, Nb-alloyed flux-cored wire electrode for high abrasive wear. The weld deposit consists of carbides of chromium and niobium. Weld metal is not machinable. The deposit should be limited to three layers. Steel, coal, cement and mineraL industry. |
| MF10-GF-65-G 62-65 HRC | C: 5.4 Cr:22 Nb: 7 B: + | High C-, Cr-, Nb-alloyed flux-cored wire electrode with special carbides giving extreme hardness. This combination results in high abrasion resistance. Applications are found in hardfacing mining equipment, augers, impellers and dredgers. |
| MF21-Gr-55-CG Matrix:47-52 HRC Carbide:>2300 HV | Fe matrix with tungsten carbide ( 62% ) | The weld metal is composed of fused tungsten carbides which are embedded in a hard matrix alloy. CARBO F-DURIT is easy to use and has little spatter and smoke. Il should be welded in no more than 2 layers using lowest possible amperage and voltage. |